Industrial High Tenacity Polyamide nylon N6 Multifilament FDY DTY POY Yarn Fiber
Polyamide (PA), nke a na-akpọkarị eriri naịlọn bụ eriri sịntetị nke mbụ pụtara n'ụwa ma bụrụ eriri plastik injin thermoplastic nwere ihe eji arụ ọrụ mara mma.Ụmụ irighiri ihe naịlọn nwere -CO- na -NH- otu, nke nwere ike ịmepụta njikọ hydrogen n'etiti ma ọ bụ n'ime ụmụ irighiri ihe, ma nwee ike jikọta ya na ụmụ irighiri ihe ndị ọzọ.Ya mere, naịlọn nwere ikike ịmị mmiri dị mma ma nwee ike ịmepụta usoro kristal ka mma.
Polyamide (PA) eriri nylon nwere ezigbo nguzogide alkali, mana nguzogide acid adịghị mma.N'okpuru ụlọ okpomọkụ nkịtị, ọ nwere ike iguzogide 7% hydrochloric acid, 20% sulfuric acid, 10% nitric acid, na 50% caustic soda ya mere fiber polyamide dabara maka uwe ọrụ mgbochi corrosion.Tụkwasị na nke a, enwere ike iji ya dị ka ụgbụ azụ azụ n'ihi nkwụsị nke mmiri mmiri.Ndụ ụgbụ azụ nke Polyamide (PA) eriri nylon dị ogologo ugboro 3 ruo 4 karịa ụgbụ azụ azụ nkịtị.
N'ihi ike ya dị elu, nkwụsi ike mmetụta na ezigbo nguzogide abrasion, ihe nketa polyamide nke eriri taya emere n'ime taya dị elu karịa nke ụdọ taya rayon.Mgbe ulechara, taya ụdọ polyamide nwere ike ịga ihe dịka 300,000km, ebe taya ụdọ rayon nwere ike ịga naanị ihe dịka 120,000 km.Ụdọ ejiri na eriri taya nwere njirimara nke ike dị elu, modul dị elu na ike ọgwụgwụ.N'ihi njikọ molekụla polyamide n'ụdị apịaji, naịlọn 66 na nylon 6 bụ polyamides.N'ezie ike na modul nke eriri na-erute 10% nke ụkpụrụ ụkpụrụ.
Ike na-agbaji nke eriri polyamide bụ 7 ~ 9.5 g / d ma ọ bụ karịa, na ike na-agbaji nke ala mmiri ya bụ ihe dịka 85% ~ 90% nke ahụ na ala akọrọ.Polyamide (PA) eriri nylon nwere nguzogide okpomọkụ na-adịghị mma nke na-atụgharị edo edo mgbe awa 5 gachara na 150 ℃ Celsius, na-amalite ịdị nro na 170 ℃ wee gbazee na 215 ℃.The okpomọkụ eguzogide nke naịlọn 66 dị mma karịa naịlọn 6. Ya mma okpomọkụ bụ 130 ℃ na karị.90 ℃.Polyamide fiber nwere ezigbo nguzogide okpomọkụ dị ala.Ọbụna ma ọ bụrụ na a na-eji ya na obere okpomọkụ nke mwepu 70 ℃, ya na-agbanwe agbanwe ọnụego adịghị agbanwe nke ukwuu.
N'ime ngwa ụlọ ọrụ mmepụta ihe, enwere ike iji polyamide (PA) eriri nylon maka ụgbụ azụ, akwa nzacha, eriri, akwa taya taya, ụlọikwuu, eriri ebu, akwa ụlọ ọrụ, wdg ma jiri ya dị ka parachutes na akwa ndị agha ndị ọzọ na nchekwa mba.
Kedu ihe kpatara ị na-ahọrọ AOPOLY Nylon Yarn?
◎ Machine: 4 ahịrị nke polymerization, 100 tent nke ogologo na-agbagọ igwe, 41 tent nke isi twisters &.twister compound, 41 nke igwe loom nke Dornier si Germany, 2 setịpụ ahịrị mgbụsị akwụkwọ, yana Sistemụ Nleba Ọdịmma Ngwaahịa
◎ Akụrụngwa: akụrụngwa ọhụrụ (ihe ụlọ & nke ebubata), masterbatches na-ebubata na mmanụ ebubata maka mmepụta
◎ Sample: ezi sample nwere ike wetara site ahịa chọrọ.
◎ Quality: elu àgwà nke iji otu ihe atụ
◎ Ike: ihe ruru.100,000ton kwa afọ
◎ Agba: ọcha ọcha, ìhè edo edo, pink
◎ MOQ: 1ton maka agba ọ bụla
◎ Nnyefe: na-abụkarị 15days maka 40HQ mgbe ị nwetasịrị nkwụnye ego
Ngwa isi
A na-ejikarị yarn Nylong6 eme ihe maka akwa naịlọn, akwa nylon, akwa naịlọn, eriri, ụgbụ azụ, wdg.
Oke
Nkọwa nke Nylon6 Industrial Yarn
| Ihe Mba | AP-N6Y-840 | AP-N6Y-1260 | AP-N6Y-1680 | AP-N6-1890 |
| Njupụta Linear (D) | 840D/140F | 1260D/210F | 1680D/280F | 1890D/315F |
| Ike na ezumike (G/D) | ≥8.8 | ≥9.1 | ≥9.3 | ≥9.3 |
| Njupụta Linear (dtex) | 930+30 | 1400+30 | 1870+30 | 2100+30 |
| Ọnụọgụ dị iche iche nke njupụta ahịrị (%) | ≤0.64 | ≤0.64 | ≤0.64 | ≤0.64 |
| Ike tensile (N) | ≥73 | ≥113 | ≥154 | ≥172 |
| Mgbatị n'oge ezumike (%) | 19-24 | 19-24 | 19-24 | 19-24 |
| Mgbatị na ibu ọkọlọtọ (%) | 12+1.5 | 12+1.5 | 12+1.5 | 12+1.5 |
| Ọnụego mgbanwe nke ike tensile (%) | ≤3.5 | ≤3.5 | ≤3.5 | ≤3.5 |
| Mgbatị ike mgbada na nkwụsị (%) | ≤5.5 | ≤5.5 | ≤5.5 | ≤5.5 |
| OPU (%) | 1.1+0.2 | 1.1+0.2 | 1.1+0.2 | 1.1+0.2 |
| Mbelata okpomọkụ 160 ℃, 2min (%) | ≤8 | ≤8 | ≤8 | ≤8 |
| Nkwụsi ike nke okpomọkụ 180 ℃, 4h (%) | ≥90 | ≥90 | ≥90 | ≥90 |
Nkọwapụta nke Nylong6 Industrial Fabric
| Nrụpụta eriri | |||||
| Ihe Mba | 840D/2 | 1260D/2 | 1260/3 | 1680D/2 | 1890D/2 |
| Ike na-agbaji (N/pc) | ≥132.3 | ≥205.8 | ≥303.8 | ≥269.5 | ≥303.8 |
| EASL 44.1N (%) | 95+0.8 | ||||
| EASL 66.6N (%) | 95+0.8 | ||||
| EASL 88.2N (%) | 95+0.8 | ||||
| EASL 100N (%) | 95+0.8 | 95+0.8 | |||
| Adhesion H-Nnwale 136℃, 50min, 3Mpa (N/cm) | ≥107.8 | ≥137.2 | ≥166.5 | ≥156.8 | ≥166.6 |
| Ọnụọgụ dị iche iche nke ike mgbaji (%) | ≤5.0 | ≤5.0 | ≤5.0 | ≤5.0 | ≤5.0 |
| Ọnụọgụ mgbanwe dị iche iche nke elongation na agbaji (%) | ≤7.5 | ≤7.5 | ≤7.5 | ≤7.5 | ≤7.5 |
| Ntupu ibu (%) | 4.5+1.0 | 4.5+1.0 | 4.5+1.0 | 4.5+1.0 | 4.5+1.0 |
| Mgbatị na agbaji (%) | 23+2.0 | 23+2.0 | 23+2.0 | 23+2.0 | 23+2.0 |
| Ihe nlele eriri (mm) | 0.55 + 0.04 | 0.65 + 0.04 | 0.78 + 0.04 | 0.75 + 0.04 | 0.78 + 0.04 |
| eriri eriri (T/m) | 460+15 | 370+15 | 320+15 | 330+15 | 320+15 |
| Nnwale mbelata 160 ℃, 2min (%) | ≤6.5 | ≤6.5 | ≤6.5 | ≤6.5 | ≤6.5 |
| Ọdịnaya mmiri (%) | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 | ≤1.0 |
| Ogologo ákwà (cm) | 145+2 | 145+2 | 145+2 | 145+2 | 145+2 |
| Ogologo ákwà (m) | 1100+50 | 1300+50 | 1270+50 | 1300+50 | 1270+50 |